Product |
Thickness of the deposit |
Main grain size |
Bead diameters |
T
E
C
H
N
O |
D
U
R |
TECHNODUR®SGT |
0.080" to 0.160" |
0.005" |
4 and 6 mm |
TECHNODUR®GT |
0.080" to 0.200" |
0.010" |
4 and 6 mm |
TECHNODUR®GN |
0.100" to 0.250" |
0.020" |
4-6 and 8 mm |
TECHNODUR®GG |
0.100" to 0.300" |
0.035" |
6 and 8 mm |
TECHNODUR®TGG |
0.150" to 0.400" |
0.060" |
6 and 8 mm |
T
E
C
H
N
O |
S
P
H
E
R
E |
TECHNOSPHERE®GF |
0.080" to 0.200" |
0.010" to 0.015" |
4 and 6 mm |
TECHNOSPHERE®GN |
0.100" to 0.250" |
0.015" to 0.030" |
4-6 and 8 mm |
TECHNOSPHERE®GG |
0.100" to 0.300" |
0.030" to 0.050" |
6 and 8 mm |
TECHNOSPHERE®TGG |
0.150" to 0.400" |
0.050" to 0.090" |
6 and 8 mm |
- Stabilizers, Drill bits, Wear pads
- mixer blades
- conveyor screws
- Scrappers
- and many other applications.
Cat. |
Item |
Crushed Carbide Hardness |
Sphérotène® Carbide Hardness |
Carbide size |
Carbide Concentration |
Base Alloy |
Alloy Hardness |
Melting point |
Deposit density |
Recom. Deposit Thickness |
Powder NiCr |
MB40 |
no |
no |
NiCr |
40 HRc |
1087 °C |
8.2 |
0.020" - 0.120" |
Powder NiCr |
TP 60 RC |
no |
no |
NiC |
60 HRc |
1038 °C |
7.8 |
0.040" - 0.080" |
Powder WC |
TP 2030 |
2000 ± 200 HV |
no |
40-100µ |
40% by weight |
NiCr |
60 HRc |
1038 °C |
10.5 |
0.040" - 0.080" |
Powder WC |
TP 40/40 |
2000 ± 200 HV |
no |
40-100µ |
40% by weight |
NiCr |
40 HRc |
1087 °C |
11.2 |
0.040" - 0.080" |
Powder WC Sphérotène® |
TP 4000 |
3000 ± 500 HV |
40-100µ |
40% by weight |
NiCr |
60 HRc |
1038 °C |
10.5 |
0.040" - 0.080" |
Powder WC Sphérotène® |
TP 4040S |
3000 ± 500 HV |
40-100µ |
40% by weight |
NiCr |
40 HRc |
1087 °C |
11.2 |
0.040" - 0.080" |
Cat. |
Item |
Crushed Carbide Hardness |
Sphérotène® Carbide Hardness |
Carbide size |
Carbide Concentration |
Base Alloy |
Alloy Hardness |
Melting point |
Deposit density |
Recom. Deposit Thickness |
Powder WC |
3000 ± 500 HV |
40-210µ |
60%by weight |
NiCr |
40 HRc |
1087 °C |
13 |
0.020" - 0.120" |
Send Inquiry :